材质单 



  COMPONENT 成分 
  RESULT 结果 

1. 
Ash content, not more % 灰分，不超过% 
  0.14 

2. 
Mass fraction of sulphur, not more % 硫的质量分数，不超过% 
Low sulphur residual oil 

低硫残油 
0.5 

3. 
Temperature of the flash, not less oC火花温度，不低于℃ 
in the closed crucible闭口坩埚 
65 

    In the open crucible oC开口坩埚，℃ 
110 min最低 

4. 
The temperature of solidification, not higher oC凝固温度，不高于℃ 
  25 

5. 
Kinematics viscosity运动粘度 
  118 max最高 

6. 
Water content含水量 
  0.5% 

7. 
Mechanical impurities机械杂质 
  Lower than低于 0.1% 

8. 
Acidity酸度 
  Lower than低于 5 mg KOH/ 100ml 

9. 
Alkalinity含碱量 
  Nil 

10. 
Gross Calorific Value总热值 Kcal/kg / KJ/kg 
  Min最低9200/41300 

11. 
Density at 15.0 deg. C Kg/l在15℃时的密度kg/l 
  0.8900-0.9200 

12. 
Hydrogen Sulfide Content (H2S) pom硫化氢含量（硫化氢）聚甲醛 
  0.5 max最高 

13. 
Carbon Residual残碳 
  Lower than低于 7% 

14. 
Vanadium钒 (V) ppm 
  23 

15. 
Aluminium 铝(Al) ppm 
  5 

16. 
Silikon硅 (Si) ppm 
  12 

17. 
Nickel 镍(Ni) ppm 
  49 

18. 
Asphaltenes 沥青质m/m 
  3.6% 

19. 
Destilation @4 mm Hg Extracted to 760 mm Hg蒸馏@4毫米汞柱，提取到760毫米汞柱 
    
    Initial Boiling Point deg. C 

初沸点℃ 
216 

    5% recovered deg. C 

恢复5%，℃ 
259 

    10% recovered deg. C 

恢复10%，℃ 
310 

    20% recovered deg. C 

恢复20%，℃ 
358 

    30% recovered deg. C 

恢复30%，℃ 
445 

    40% recovered deg. C 

恢复40%，℃ 
502 

    50% recovered deg. C 

恢复50%，℃ 
534 

    60% recovered deg. C 

恢复60%，℃ 
538 

    75% recovered deg. C 

恢复75%，℃ 
545 

    80% recovered deg. C 

恢复80%，℃ 
  
    90% recovered deg. C 

恢复90%，℃ 
  
20 
Final Boiling point deg. C 最终沸点 
  550 

21 
Percent Recovered vol 回收体积 
  78% 

22 
  Residue vol 残留提及 
  22% 

23 
COMPONENT 成分 
  RESULT 

24 
Total Nitrogen m/m 总氮 
  0.19% 

25 
20. Sodium (Na) ppm 钠 
  15