TYPICAL PROPERTIES (1) |
MECHANICAL
|
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min
|
490
|
kgf/cm²
|
ASTM D 638
|
Tensile Stress, brk, Type I, 50 mm/min
|
400
|
kgf/cm²
|
ASTM D 638
|
Tensile Strain, yld, Type I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
Tensile Strain, brk, Type I, 50 mm/min
|
50
|
%
|
ASTM D 638
|
Tensile Modulus, 50 mm/min
|
20000
|
kgf/cm²
|
ASTM D 638
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
800
|
kgf/cm²
|
ASTM D 790
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
20300
|
kgf/cm²
|
ASTM D 790
|
IMPACT
|
Value |
Unit |
Standard |
Izod Impact, notched, 23°C
|
68
|
cm-kgf/cm
|
ASTM D 256
|
Instrumented Impact Total Energy, 23°C
|
506
|
cm-kgf
|
ASTM D 3763
|
THERMAL
|
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50
|
135
|
°C
|
ASTM D 1525
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
126
|
°C
|
ASTM D 648
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
85
|
°C
|
ASTM D 648
|
CTE, -40°C to 40°C, flow
|
7.92E-05
|
1/°C
|
ASTM E 831
|
CTE, -40°C to 40°C, xflow
|
8.64E-05
|
1/°C
|
ASTM E 831
|
Relative Temp Index, Elec
|
100
|
°C
|
UL 746B
|
Relative Temp Index, Mech w/impact
|
85
|
°C
|
UL 746B
|
Relative Temp Index, Mech w/o impact
|
100
|
°C
|
UL 746B
|
PHYSICAL
|
Value |
Unit |
Standard |
Specific Gravity
|
1.3
|
-
|
ASTM D 792
|
Mold Shrinkage, flow, 3.2 mm (5)
|
1.2 - 1.4
|
%
|
SABIC Method
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
1.2 - 1.4
|
%
|
SABIC Method
|
Melt Flow Rate, 266°C/5.0 kgf
|
19
|
g/10 min
|
ASTM D 1238
|
Melt Volume Rate, MVR at 265°C/5.0 kg
|
17
|
cm³/10 min
|
ISO 1133
|
ELECTRICAL
|
Value |
Unit |
Standard |
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
High Voltage Arc Track Rate {PLC}
|
4
|
PLC Code
|
UL 746A
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
Comparative Tracking Index (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
FLAME CHARACTERISTICS
|
Value |
Unit |
Standard |
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
UL Recognized, 94-5VA Rating (3)
|
2.49
|
mm
|
UL 94
|