XENOY™ Resin 5220U

SI

| British

| Metric

| PDF

Americas: COMMERCIAL

Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance.

Property

MECHANICAL

Tensile Stress, yld, Type I, 50 mm/min

540

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

520

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

4

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

120

%

ASTM D 638

Tensile Modulus, 50 mm/min

22900

kgf/cm²

ASTM D 638

Tensile Modulus, 5 mm/min

22900

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

850

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

20600

kgf/cm²

ASTM D 790

Tensile Stress, yield, 50 mm/min

50

MPa

ISO 527

Tensile Stress, break, 50 mm/min

50

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

4

%

ISO 527

Tensile Strain, break, 50 mm/min

120

%

ISO 527

Tensile Modulus, 1 mm/min

2050

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

80

MPa

ISO 178

Flexural Modulus, 2 mm/min

2000

MPa

ISO 178

IMPACT

Izod Impact, notched, 23°C

72

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

54

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -40°C

30

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

611

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

50

kJ/m²

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

30

kJ/m²

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

55

kJ/m²

ISO 179/1eA

THERMAL

Vicat Softening Temp, Rate B/50

122

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

84

°C

ASTM D 648

HDT, 0.45 MPa, 6.4 mm, unannealed

107

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

99

°C

ASTM D 648

CTE, -40°C to 40°C, flow

9.5E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

9.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

9.5E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

9.E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/50

120

°C

ISO 306

Vicat Softening Temp, Rate B/120

125

°C

ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

75

°C

ISO 75/Af

Relative Temp Index, Elec

75

°C

UL 746B

Relative Temp Index, Mech w/impact

75

°C

UL 746B

Relative Temp Index, Mech w/o impact

75

°C

UL 746B

PHYSICAL

Specific Gravity

1.21

-

ASTM D 792

Specific Volume

0.83

cm³/g

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.8 - 1

%

SABIC Method

Mold Shrinkage on Tensile Bar, xflow (2) (5)

0.8 - 1

%

SABIC Method

Density

1.22

g/cm³

ISO 1183

Water Absorption, (23°C/sat)

0.5

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.15

%

ISO 62

Melt Flow Rate, 250°C/5.0 kg

16

g/10 min

ISO 1133

Melt Volume Rate, MVR at 250°C/5.0 kg

15

cm³/10 min

ISO 1133

ELECTRICAL

Arc Resistance, Tungsten {PLC}

5

PLC Code

ASTM D 495

Hot Wire Ignition {PLC)

3

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC}

0

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC}

1

PLC Code

UL 746A

FLAME CHARACTERISTICS

UL Recognized, 94HB Flame Class Rating (3)

1.5

mm

UL 94

UV-light, water exposure/immersion

F2

-

UL 746C

Source GMD, last updated:2011/06/08

Processing

Injection Molding

Drying Temperature

110

°C

Drying Time

4 - 6

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

260 - 275

°C

Nozzle Temperature

255 - 270

°C

Front - Zone 3 Temperature

255 - 275

°C

Middle - Zone 2 Temperature

250 - 270

°C

Rear - Zone 1 Temperature

245 - 265

°C

Mold Temperature

65 - 90

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

50 - 80

rpm

Shot to Cylinder Size

50 - 80

%

Vent Depth

0.013 - 0.02

mm

Sheet Extrusion

Drying Temperature

110 - 115

°C

Drying Time

4 - 6

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0 - 0.02

%

Melt Temperature

245 - 275

°C

Barrel - Zone 1 Temperature

170 - 205

°C

Barrel - Zone 2 Temperature

195 - 255

°C

Barrel - Zone 3 Temperature

205 - 280

°C

Barrel - Zone 4 Temperature

205 - 280

°C

Adapter Temperature

225 - 280

°C

Die Temperature

230 - 280

°C

Roll Stack Temp - Top

70 - 80

°C

Roll Stack Temp - Middle

75 - 80

°C

Roll Stack Temp - Bottom

80 - 95

°C