TYPICAL PROPERTIES (1) |
MECHANICAL
|
Value |
Unit |
Standard |
Tensile Stress, yld, Type I, 50 mm/min
|
490
|
kgf/cm²
|
ASTM D 638
|
Tensile Stress, brk, Type I, 50 mm/min
|
420
|
kgf/cm²
|
ASTM D 638
|
Tensile Strain, yld, Type I, 50 mm/min
|
4.9
|
%
|
ASTM D 638
|
Tensile Strain, brk, Type I, 50 mm/min
|
74
|
%
|
ASTM D 638
|
Tensile Modulus, 5 mm/min
|
20400
|
kgf/cm²
|
ASTM D 638
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
760
|
kgf/cm²
|
ASTM D 790
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
21400
|
kgf/cm²
|
ASTM D 790
|
Tensile Stress, yield, 50 mm/min
|
48
|
MPa
|
ISO 527
|
Tensile Stress, break, 50 mm/min
|
40
|
MPa
|
ISO 527
|
Tensile Strain, yield, 50 mm/min
|
4.6
|
%
|
ISO 527
|
Tensile Strain, break, 50 mm/min
|
74.8
|
%
|
ISO 527
|
Tensile Modulus, 1 mm/min
|
2190
|
MPa
|
ISO 527
|
Flexural Stress, yield, 2 mm/min
|
73
|
MPa
|
ISO 178
|
Flexural Modulus, 2 mm/min
|
2050
|
MPa
|
ISO 178
|
IMPACT
|
Value |
Unit |
Standard |
Izod Impact, notched, 23°C
|
49
|
cm-kgf/cm
|
ASTM D 256
|
Izod Impact, notched, -30°C
|
17
|
cm-kgf/cm
|
ASTM D 256
|
Instrumented Impact Total Energy, 23°C
|
509
|
cm-kgf
|
ASTM D 3763
|
Izod Impact, notched 80*10*4 +23°C
|
31
|
kJ/m²
|
ISO 180/1A
|
Izod Impact, notched 80*10*4 -30°C
|
10
|
kJ/m²
|
ISO 180/1A
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
34
|
kJ/m²
|
ISO 179/1eA
|
THERMAL
|
Value |
Unit |
Standard |
Vicat Softening Temp, Rate B/50
|
130
|
°C
|
ASTM D 1525
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
127
|
°C
|
ASTM D 648
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
88
|
°C
|
ASTM D 648
|
CTE, -40°C to 40°C, flow
|
8.16E-05
|
1/°C
|
ASTM E 831
|
CTE, -40°C to 40°C, xflow
|
9.74E-05
|
1/°C
|
ASTM E 831
|
CTE, -40°C to 40°C, flow
|
8.16E-05
|
1/°C
|
ISO 11359-2
|
CTE, -40°C to 40°C, xflow
|
9.74E-05
|
1/°C
|
ISO 11359-2
|
Vicat Softening Temp, Rate B/50
|
130
|
°C
|
ISO 306
|
Vicat Softening Temp, Rate B/120
|
133
|
°C
|
ISO 306
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
122
|
°C
|
ISO 75/Bf
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
84
|
°C
|
ISO 75/Af
|
Relative Temp Index, Elec
|
120
|
°C
|
UL 746B
|
Relative Temp Index, Mech w/impact
|
120
|
°C
|
UL 746B
|
Relative Temp Index, Mech w/o impact
|
140
|
°C
|
UL 746B
|
PHYSICAL
|
Value |
Unit |
Standard |
Specific Gravity
|
1.35
|
-
|
ASTM D 792
|
Mold Shrinkage, flow, 3.2 mm (5)
|
1.1 - 1.4
|
%
|
SABIC Method
|
Melt Flow Rate, 250°C/5.0 kgf
|
9.3
|
g/10 min
|
ASTM D 1238
|
Density
|
1.34
|
g/cm³
|
ISO 1183
|
Water Absorption, (23°C/sat)
|
0.08
|
%
|
ISO 62
|
Moisture Absorption (23°C / 50% RH)
|
0.08
|
%
|
ISO 62
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
7
|
cm³/10 min
|
ISO 1133
|
ELECTRICAL
|
Value |
Unit |
Standard |
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
High Voltage Arc Track Rate {PLC}
|
4
|
PLC Code
|
UL 746A
|
High Voltage Arc Resistance {PLC)
|
6
|
PLC Code
|
UL 746A
|
High Ampere Arc Ign, surface {PLC}
|
3
|
PLC Code
|
UL 746A
|
Comparative Tracking Index (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
FLAME CHARACTERISTICS
|
Value |
Unit |
Standard |
UL Compliant, 94V-0 Flame Class Rating (3)(4)
|
0.63
|
mm
|
UL 94 by SABIC-IP
|
UL Compliant, 94-5VA Rating (3)(4)
|
3
|
mm
|
UL 94 by SABIC-IP
|